Heat Insulation Panel Hot Melt Adhesive Resin Aluminum Plastic Panel

Grade:VF790

Product: Hot Melt Adhesive Resin For Aluminum Plastic Panel And Heat Insulation Panel

Descriptions

VF790 is a maleic anhydride and vinyl acetate functionalized polyethylene mixture, easy to form film, with excellent processability and adhesive strength.

In the last two decades, new structural hot melts have been developed that overcome some of the drawbacks and limitations of traditional hot melts. These new adhesives have been designed to reduce manufacturing cost and to improve manufacturing efficiency. The newest classes of hot melts are reactive urethanes and silicones. These types of hot melts combine the advantages of traditional hot melts with those of reactive structural adhesives. They undergo a secondary moisture cure upon cooling or are cured by ultraviolet radiation that causes the adhesive to crosslink which provides higher strength and flexibility and results in more durable bonds.

Mechanical Properties

Thermal Properties

Note:The datas is used for referential purpose only, not for quality commitment.

Advantages

1. Good film forming performance, can be formed into 0.02 ㎜ thick film;
2. High adhesive strength, good durability, excellent adhesive interface performance, showing the interface adhesive cohesion energy destruction;
3. Can withstand a certain acid, alkali, salt spray and other chemical solvent corrosion;
4. Strong adaptability, can meet the needs of high-speed production;
5. Good weather resistance, adapt to the climate temperature change environment, can be outdoor use.

Chemical Structure

Composition: Maleic Anhydride and Vinyl Acetate functionalized polyethylene mixture.

Application

VF790 is widely used as binder for aluminum plastic panel and heat insulation panel.

Statement: the above processing technology shall be different according to different conditions such as product size, mold design and processing equipment specification, and the details shall be adjusted according to the actual situation.